Compare Steel alloys for CNC machining custom parts
Renowned for its strength, durability, and versatility, steel is the go-to material for engineers and designers seeking reliability and performance in machined parts. Unlike other materials, steel offers unparalleled durability and resistance to wear, ensuring that components withstand the test of time in even the most demanding applications.
Its hardness and machinability allow for intricate detailing and tight tolerances, resulting in superior-quality parts that meet the most rigorous standards. From automotive gears to industrial machinery components, steel delivers unmatched performance and reliability.
Choose steel for your next machining project and experience the unmatched durability, precision, and versatility that only steel can provide.
Steel 1018
Tensile Strength (MPa) 370 MPa
Shear Modulus (GPa) 78 GPa
Elongation (%) 15%
Hardness (HB) 126 HB
Density (g/cm^3) 7.87
Steel A36
Tensile Strength (MPa) 250 MPa
Shear Modulus (GPa) 79.3 GPa
Elongation (%) 20%
Hardness (HB) 119 HB
Density (g/cm^3) 7.85
Steel 4130
Tensile Strength (MPa) 435 MPa
Shear Modulus (GPa) 80 GPa
Elongation (%) 25.5%
Hardness (HB) 197 HB
Density (g/cm^3) 7.85
Steel A36
Tensile Strength (MPa) 250 MPa
Shear Modulus (GPa) 79.3 GPa
Elongation (%) 20%
Hardness (HB) 119 HB
Density (g/cm^3) 7.85
Steel 4140
Tensile Strength (MPa) 675 MPa
Shear Modulus (GPa) 80 GPa
Elongation (%) 17.8%
Hardness (HB) 302 HB
Density (g/cm^3) 7.85
Steel 1215
Tensile Strength (MPa) 415 MPa
Shear Modulus (GPa) 80 GPa
Elongation (%) 10%
Hardness (HB) 167 HB
Density (g/cm^3) 7.87
Steel 4140 PH
Tensile Strength (MPa) 685-896 MPa
Shear Modulus (GPa) 80 GPa
Elongation (%) 14-19.2%
Hardness (HB) 271-301 HB
Density (g/cm^3) 7.85
Steel 4340
Tensile Strength (MPa) 470 MPa
Shear Modulus (GPa) 74 GPa
Elongation (%) 22%
Hardness (HB) 217 HB
Density (g/cm^3) 7.85